Izod impact testing is an ASTM standard method of determining the impact resistance of materials. A pivoting arm is raised to a specific height (constant potential energy) and then released. The arm swings down hitting the sample, breaking the specimen. The energy absorbed by the sample is calculated from the height the arm swings to after hitting the sample. A notched sample is generally used to determine impact energy and notch sensitivity.
Contents
The test is similar to the Charpy impact test but uses a different arrangement of the specimen under test. The Izod impact test differs from the Charpy impact test in that the sample is held in a cantilevered beam configuration as opposed to a three-point bending configuration.
The test is named after the English engineer Edwin Gilbert Izod (1876–1946), who described it in his 1903 address to the British Association, subsequently published in Engineering.
Impact energy
Impact is a very important phenomenon in governing the life of a structure. For example, in the case of an aircraft, impact can take place by a bird hitting a plane while it is cruising, or during take off and landing the aircraft may be struck by debris that is present on the runway, and as well as other causes. It must also be calculated for roads if speed breakers are present, in bridge construction where vehicles punch an impact load, etc.
Impact tests are used in studying the toughness of material. A material's toughness is a factor of its ability to absorb energy during plastic deformation. Brittle materials have low toughness as a result of the small amount of plastic deformation that they can endure. The impact value of a material can also change with temperature. Generally, at lower temperatures, the impact energy of a material is decreased. The size of the specimen may also affect the value of the Izod impact test because it may allow a different number of imperfections in the material, which can act as stress risers and lower the impact energy.
ASTM test for plastics
The ASTM International standard for Izod Impact testing of plastics is ASTM D256. The results are expressed in energy lost per unit of thickness (such as ft·lb/in or J/cm) at the notch. Alternatively, the results may be reported as energy lost per unit cross-sectional area at the notch (J/m2 or ft·lb/in2). In Europe, ISO 180 methods are used and results are based only on the cross-sectional area at the notch (J/m2). The dimensions of a standard specimen for ASTM D256 are 63.5 × 12.7 × 3.2 mm (2.5 × 0.5 × 0.125 in). The most common specimen thickness is 3.2 mm (0.13 in), but the width can vary between 3.0 and 12.7 mm (0.12 and 0.50 in).