Lithium hybrid organic battery

PAni/V2O5

Oxides, like V₂O₅, are used as cathodes in rechargeable lithium batteries. Crystalline V₂O₅ has a weaker rechargeability or cyclability than amorphous V₂O₅ because the crystal structure is damaged during discharge/charge cycles. However, amorphous oxides, in particular the V₂O₅ xerogel, allows lithium ion to diffuse faster and thus have a better cyclability. Hybrid is formed by combining a conducting organic polymer (e.g. polyaniline) with an oxide (e.g. V₂O₅).

V₂O₅ gels are prepared using the ion-exchange method. Vanadium (V) polymerizes aniline. Before synthesis of a hybrid battery, potentiometric titration of V₂O₅ gel with (NH₄)₂Fe(SO₄)₂*6H₂O is carried out; this determines the amount of V(V) present in the gel. Aniline solution is slowly added onto the V₂O₅*nH₂O gel. The following procedure is demonstrated in Figure 3.

V₂O₅ is used because of its high specific capacity, high thermal stability, and high structural flexibility with lithium. Up to three moles of lithium ions can be added into the V₂O₅ lattice to create different structures. The structures created give the hybrid a long battery life. However, the intercalation capacity depends on the moderate electrical conductivity and low diffusion coefficient of the lithium ions in the vanadium oxide matrix.

Polyaniline is easily produced to have controlled structural and electronic properties. Polyaniline eliminates the coordinated water of the V₂O₅ xerogel, so more lithium ions can be integrated into the structure. The organic part of the PAni/V₂O₅ hybrid degrades with the increase of temperature.

V(V) is reduced to V(IV), and aniline is oxidized to polyaniline. Re-oxidizing V(IV) to a higher oxidation state of V(V) increases initial cell voltage and specific capacity. Since polyaniline is an electrochemically active component, it improves the specific charge of the hybrid material. Combining polyaniline with V₂O₅ yields a larger specific charge difference. Thus, a greater total capacity contribution than V₂O₅ alone. Furthermore, the hybrid has a higher specific capacity than that of the V₂O₅ xerogel. Electrical conductivity is as high as 0.09 S/cm for 15 days.

As a result, PAni/V₂O₅ hybrid is a conducting network and an electroactive material in the composites, which improves electrochemical behavior. It also prevents the irreversible structural changes made by redox cycling when the lithium ions enter the lattice. Moreover, this hybrid also has a high specific capacity and improved cyclability without capacity deterioration.

PTMA/LiFePO4

PTMA is an organic nitroxide radical electrode-active polymer, and LiFePO₄ is the inorganic electrode-active material. PTMA is used because it has a high capacity and a long cycle life. To synthesize organic radical-inorganic hybrid electrodes, electrode environments for each component must be optimized. PTMA and LiFePO₄ were combined with entire PTMA and LiFePO₄ electrode with different weight ratios: 25/75, 50/50, and 75/25.

The cell was prepared by using a working electrode to assemble a half-cell configuration dry glove box with Li metal as an anode, ethyl carbonate/dimethyl carbonate as an electrophile, and a Celgard 3501 membrane as a separator. Using Arbin BT-200 Battery Tester, the cell was electrochemically cycled at room temperature. By using a Solarton workstation, the cyclic voltammetry and electrochemical impedance spectroscopy of cells were performed. A focus ion beam-scanning electron microscope was used to determine the morphology of the electrodes before and after the high rate pulse discharge (HRPD) cycling.

After testing, pure PTMA and LiFePO₄ electrode give a sharp redox peak and decrease the voltage gap between oxidation and reduction. Therefore, PTMA and LiFePO₄ improve the rate and reversibility of the redox couples. Furthermore, the hybrid cathodes have a lower charge-transfer resistance, allowing easier migration of Li ions through the electrode interface. Moreover, PTMA/LiFePO₄ has a longer life cycle compared to pure LiFePO₄ or PTMA systems.